Tez No İndirme Tez Künye Durumu
213816
2-[(pridin-3-il-metilen)amino]fenolün yükseltgen polimerizasyonu / Oxidative polimerization of 2-[(pyridine-3-yl-methylene)amino]phenol
Yazar:DERYA EMDİ
Danışman: PROF.DR. MEHMET SAÇAK
Yer Bilgisi: Ankara Üniversitesi / Fen Bilimleri Enstitüsü / Kimya Ana Bilim Dalı
Konu:Polimer Bilim ve Teknolojisi = Polymer Science and Technology
Dizin:Metal kompleksleri = Metal complexes ; Oksidatif polikondenzasyon = Oxidative polycondensation ; Termal analiz = Thermal analysis 		Onaylandı
Yüksek Lisans
Türkçe
2007
122 s.
2-[(Pridin-3-İl-Metilen)Amino]Fenol (2-PMAP)'ün polimeri, bazik ortamda, yükseltgen olarak hava oksijeni kullanılarak oksidatif polikondensasyon reaksiyonu ile sentezlendi. Prosesin temel değerleri ve optimum reaksiyon koşulları belirlendi. Polimerin verimi %71,38 olarak bulundu. Sentezlenen monomer ve polimerin yapıları, FTIR, UV, 1H-13C-NMR ve elementel analiz yöntemleri ile aydınlatıldı. FTIR, 1H-NMR ve 13C-NMR verilerine göre; polimerizasyon, 2-PMAP'in -OH gruplarına göre, orto ve para konumlarından gerçekleşmektedir. Mol kütlesi dağılım değerleri ise GPC ölçümleri ile belirlenmiştir. Poli-2- PMAP'in sayıca ortalama mol kütlesi(Mn), kütlece ortalama mol kütlesi (Mw) ve heterojenlik indisi sırasıyla 7150, 8000 g mol-1 ve 1,119 olarak bulunmuştur. 2-PMAP, 2-PMAP-Cd, 2- PMAP-Co, 2-PMAP-Cu, 2-PMAP-Zn, Poli-2-PMAP, Poli-2-PMAP-Cd, Poli-2-PMAP-Co, Poli-2-PMAP-Cu ve Poli-2-PMAP-Zn monomer/polimer-metal komplekslerinin termal analizleri 15-1000°C arasında N2 atmosferinde incelenmiştir. Sentezlenen maddelerin antimikrobiyal aktiviteleri incelenmiştir. Anahtar Kelimeler: Oksidatif polikondensasyon, 2-[(Pridin-3-İl-Metilen)Amino]fenol, monomer ve metal kompleksleri, termal analiz.
The oxidative polycondensation of 2-[(pyridine-3-yl-methylene)amino]phenol (2-PMAP) has been accomplished by using air O2 oxidant in aqueous alkaline medium. Optimum reaction conditions of the oxidative polycondensation and the main parameters of the process were established. At optimum reaction conditions, yield of the products was found to be 71.38%. The structures of the obtained monomer and polymer were confirmed by FT-IR, UV-vis, 1HNMR, 13C-NMR and elemental analysis. The characterization was made by TGA-DTA, using gel permeation chromatography (GPC) and solubility tests. The FT-IR, 1H-NMR and 13CNMR data show that the polymerization proceeded by the C-C coupling of ortho and para positions according to ?OH group of 2-[(pyridine-3-yl-methylene) amino]phenol. The molecular weight distribution values of the product were determined by GPC. The numberaverage molecular weight (Mn), weight-average molecular weight (Mw) and polydispersity index (PDI) values of Poli-2-PMAP were found to be 7150, 8000 g mol-1 and 1,119 for air O2 oxidant, respectively. Thermal analysis results of Poli-2-PMAP demonstrated to be stability against thermal decomposition. Thermal analyses of 2-PMAP, 2-PMAP-Cd, 2-PMAP-Co, 2- PMAP-Cu, 2-PMAP-Zn, Poli-2-PMAP, Poli-2-PMAP-Cd, Poli-2-PMAP-Co, Poli-2-PMAPCu and Poli-2-PMAP-Zn monomer/polymer-metal complex compounds were investigated in a N2 atmosphere between 15-1000°C. Antibacteria and antifungal activities of synthesized compounds were examined against some selected bacteria and fungus. Key words: Oxidative polycondensation, 2-[(pyridine-3-yl-methylene) amino]phenol, monomer and metal complexes, thermal degradation.